Compared to standard conditions for BrazeTec 
4576


Get more information

Your advantages at a glance:

BrazeTec BlueBraze guarantees a substantial reduction of silver content – up to 21 percent less in weight. As a result of this, you permanently lower your cost of materials, thereby getting more planning stability and independence from the fluctuations in the prices of precious metals.

Since BrazeTec BlueBraze brazing alloys have the same processing temperatures as our standard filler metals, neither processes nor constructions must be changed. Processing takes place as usual.

Considerably more brazing material per kilogram brazing alloy – thanks to the lower density of BrazeTec BlueBraze, you get approx. 10 meters more brazing rods per kilogram. The annual quantity of brazing alloy you need is therefore reduced by about 4 percent.

Brazing is BrazeTec
Brazing is BrazeTech

Address


Company*

Department

Gender*

Surename

Name*

Phone*

E-mail*

Street

Nr.

Postal code

City

Comment*mandatory

Product






 
 
 
 
 
 
Compared to standard conditions for BrazeTec 
4576
 

=
Security code. Please enter the total sum.

Silver brazing alloys, cadmium free in comparison: BrazeTec Bluebraze 2410 vs. Standard BrazeTec 3476

BrazeTec BlueBraze 2410

Composition in wt.%
Ag: 24 | Cu: 43.7 | Zn: 20 | Sn: 2 | Mn: 10 | Si: 0.3

Permitted impurity max. in wt.%
Al: 0.001 | Bi: 0.030 | Cd: 0.010 | P: 0.008 |
Pb: 0.025

Overall impurity max. in wt.%
0.15

Melting range acc. to ISO 17672 in °C
Not applicable, Why?

Melting range acc. to DSC measurement in °C
690 – 750

Brazing temperature min. in °C
750

Tensile strength acc. to DIN EN 12797 in MPa
on S 235: 330 | on E 295: 480

Density in g/cm³
8.4

Maximum elongation at break A 100 in %
17

Electrical conductivity in m/Ωmm²
2.4

 

Less silver
–10 wt.%









Same
temperature

More brazing alloy
+5.5 %
+3.6 m/kg
 
Less costs

Quotation

Wire/Rod Ø 1.5 mm
Standard BrazeTec 3476

Composition in wt.%
Ag: 34 | Cu: 36 | Zn: 27.5 | Sn: 2.5 | Mn: – | Si: –

Permitted impurity max. in wt.%
Al: 0.001 | Bi: 0.030 | Cd: 0.010 | P: 0.008 |
Pb: 0.025 | Si: 0.050

Overall impurity max. in wt.% 
0.15

Melting range acc. to ISO 17672 in °C
630 – 730

Melting range acc. to DSC measurement in °C
655 – 745

Brazing temperature min. in °C
745

Tensile strength acc. to DIN EN 12797 in MPa
on S 235: 360 | on E 295: 480

Density in g/cm³
8.9

Maximum elongation at break A 100 %
11

Electrical conductivity in m/Ωmm²
14.0

 

Silver brazing alloys, cadmium free in comparison: BrazeTec Bluebraze 2010 vs. Standard BrazeTec 3076

BrazeTec BlueBraze 2010

Composition in wt.%
Ag: 20 | Cu: 42.8 | Zn: 25 | Mn: 10 | Sn: – | In: 2 | Si: 0.3

Permitted impurity max. in wt.%
Al: 0.001 | Bi: 0.030 | Cd: 0.010 | P: 0.008 |
Pb: 0.025

Overall impurity max. in wt.%
0.15

Melting range acc. to ISO 17672 in °C
Not applicable, Why?

Melting range acc. to DSC measurement in °C
710 – 765

Brazing temperature min. in °C
765

Tensile strength acc. to DIN EN 12797 in MPa
on S 235: 300 | on E 295: 440

Density in g/cm&sup3
8.3

Maximum elongation at break A 100 in %
17

Electrical conductivity in m/Ωmm&sup2
2.7

 

Less silver
–10 wt.%









Same
temperature

More brazing alloy
+5.7 %
+3.9 m/kg
 
Less costs

Quotation

Wire/Rod Ø 1.5 mm
Standard BrazeTec 3076

Composition in wt.%
Ag: 30 | Cu: 36 | Zn: 32 | Mn: – | Sn: 2 | In: – | Si: –

Permitted impurity max. in wt.%
Al: 0.001 | Bi: 0.030 | Cd: 0.010 | P: 0.008 |
Pb: 0.025 | Si: 0.050

Overall impurity max. in wt.% 
0.15

Melting range acc. to ISO 17672 in °C
665 – 755

Melting range acc. to DSC measurement in °C
675 – 760

Brazing temperature min. in °C
760

Tensile strength acc. to DIN EN 12797 in MPa
on S 235: 360 | on E 295: 480

Density in g/cm&sup3
8.8

Maximum elongation at break A 100 %
11

Electrical conductivity in m/Ωmm&sup2
12.0

 

Silver brazing alloys, cadmium free in comparison: BrazeTec Bluebraze 3510 vs. Standard BrazeTec 4576

BrazeTec BlueBraze 3510

Composition in wt.%
Ag: 35 | Cu: 32.6 | Zn: 20 | Sn: 2 | Mn: 10 | Si: 0.4

Permitted impurity max. in wt.%
Al: 0.001 | Bi: 0.030 | Cd: 0.010 | P: 0.008 |
Pb: 0.025

Overall impurity max. in wt.%
0.15

Melting range acc. to ISO 17672 in °C
Not applicable, Why?

Melting range acc. to DSC measurement in °C
680 – 700

Brazing temperature min. in °C
700

Tensile strength acc. to DIN EN 12797 in MPa
on S 235: 320 | on E 295: 420

Density in g/cm³
8.6

Maximum elongation at break A 100 in %
14

Electrical conductivity in m/Ωmm²
2.4

 

Less silver
–10 wt.%









Same
temperature

More brazing alloy
+5.5 %
+3.6 m/kg
 
Less costs

Quotation

Wire/Rod Ø 1.5 mm
Standard BrazeTec 4576

Composition in wt.%
Ag: 45 | Cu: 27 | Zn: 25.5 | Sn: 2.5 | Mn: – | Si: –

Permitted impurity max. in wt.%
Al: 0.001 | Bi: 0.030 | Cd: 0.010 | P: 0.008 |
Pb: 0.025 | Si: 0.050

Overall impurity max. in wt.%
0.15

Melting range acc. to ISO 17672 in °C
640 – 680

Melting range acc. to DSC measurement in °C
645 – 695

Brazing temperature min. in °C
695

Tensile strength acc. to DIN EN 12797 in MPa
on S 235: 350 | on E 295: 430

Density in g/cm³
9.1

Maximum elongation at break A 100 in %
23

Electrical conductivity in m/Ωmm²
13.0

 

Silver brazing alloys, cadmium free in comparison: BrazeTec Bluebraze 3010 vs. Standard BrazeTec 4076

BrazeTec BlueBraze 3010

Composition in wt.%
Ag: 30 | Cu: 37.8 | Zn: 20 | Mn: 10 | Sn: 2 | Si: 0.2

Permitted impurity max. in wt.%
Al: 0.001 | Bi: 0.030 | Cd: 0.010 | P: 0.008 |
Pb: 0.025

Overall impurity max. in wt.%
0.15

Melting range acc. to ISO 17672 in °C
Not applicable, Why?

Melting range acc. to DSC measurement in °C
690 – 730

Brazing temperature min. in °C
730

Tensile strength acc. to DIN EN 12797 in MPa
on S 235: 350 | on E 295: 440

Density in g/cm³
8.4

Maximum elongation at break A 100 in %
14

Electrical conductivity in m/Ωmm²
2.4

 

Less silver
–10 wt.%









Same
temperature

More brazing alloy
+6.7 %
+4.5 m/kg
 
Less costs

Quotation

Wire/Rod Ø 1.5 mm
Standard BrazeTec 4076

Composition in wt.%
Ag: 40 | Cu: 30 | Zn: 28 | Mn: – | Sn: 2 | Si: –

Permitted impurity max. in wt.%
Al: 0.001 | Bi: 0.030 | Cd: 0.010 | P: 0.008 |
Pb: 0.025 | Si: 0.050

Overall impurity max. in wt.%
0.15

Melting range acc. to ISO 17672 in °C
650 – 710

Melting range acc. to DSC measurement in °C
665 – 725

Brazing temperature min. in °C
725

Tensile strength acc. to DIN EN 12797 in MPa
on S 235: 350 | on E 295: 430

Density in g/cm³
9.0

Maximum elongation at break A 100 in %
23

Electrical conductivity in m/Ωmm²
11.0

 

Silver brazing alloys, cadmium free in comparison: BrazeTec Bluebraze 2810 vs. Standard BrazeTec 4900

BrazeTec BlueBraze 2810

Composition in wt.%
Ag: 28 | Cu: 39.0 | Zn: 20 | Mn: 10 | Ni: 1 | In: 2

Permitted impurity max. in wt.%
Al: 0.001 | Bi: 0.030 | Cd: 0.010 | P: 0.008 |
Pb: 0.025 | Si: 0.05

Overall impurity max. in wt.%
0.15

Melting range acc. to ISO 17672 in °C
Not applicable, Why?

Melting range acc. to DSC measurement in °C
680 – 760

Brazing temperature min. in °C
710

Shear strength¹ acc. to DIN EN 12797 in MPa
> 250

Density in g/cm³
8.5

 

 

1) Measured according to BrazeTec standard, compound 1.2210 & K10

Less Silver
–21 wt. %










Same
Strength

More Brazing Alloy
+4.2 %
 
Less
Costs

Quatation

.
Standard BrazeTec 4900

Composition in wt.%
Ag: 49 | Cu: 16 | Zn: 23 | Mn: 7.5 | NI: 4.5 | In: –

Permitted impurity max. in wt.%
Al: 0.001 | Bi: 0.030 | Cd: 0.010 | P: 0.008 |
Pb: 0.025 | Si: 0.05

Overall impurity max. in wt.%
0.3

Melting range acc. to ISO 17672 in °C
680 – 705

Melting range acc. to DSC measurement in °C
680 – 705

Brazing temperature min. in °C
690

Shear strength¹ acc. to DIN EN 12797 in MPa
> 250

Density in g/cm³
8.9

 

 


Silver brazing alloys, cadmium free in comparison: BrazeTec Bluebraze 2810 vs. Standard BrazeTec 5081

BrazeTec BlueBraze 2810

Composition in wt.%
Ag: 28 | Cu: 39.0 | Zn: 20 | Mn: 10 | Ni: 1 | In: 2

Permitted impurity max. in wt.%
Al: 0.001 | Bi: 0.030 | Cd: 0.010 | P: 0.008 |
Pb: 0.025 | Si: 0.05

Overall impurity max. in wt.%
0.15

Melting range acc. to ISO 17672 in °C
Not applicable, Why?

Melting range acc. to DSC measurement in °C
680 – 760

Brazing temperature min. in °C
710

Shear strength¹ acc. to DIN EN 12797 in MPa
> 250

Density in g/cm³
8.5

 

 

1) Measured according to BrazeTec standard, compound 1.2210 & K10

Less Silver
–22 wt. %










Same
Strength

More Brazing Alloy
+7.6 %
 
Less
Costs

Quotation

.
Standard BrazeTec 5081

Composition in wt.%
Ag: 50 | Cu: 20 | Zn: 28 | Mn: – | NI: 2 | In: –

Permitted impurity max. in wt.%
Al: 0.001 | Bi: 0.030 | Cd: 0.010 | P: 0.008 |
Pb: 0.025 | Si: 0.05

Overall impurity max. in wt.%
0.3

Melting range acc. to ISO 17672 in °C
660 – 715

Melting range acc. to DSC measurement in °C
670 – 730

Brazing temperature min. in °C
730

Shear strength¹ acc. to DIN EN 12797 in MPa
> 230

Density in g/cm³
9.2

 

 


Sandwich alloys, Cd free in comparison: BrazeTec Bluebraze 28/Cu vs. Standard BrazeTec 49/Cu

BrazeTec BlueBraze 28/Cu

Composition¹ in wt.%
Ag: 28 | Cu: 39.0 | Zn: 20 | Mn: 10 | Ni: 1 | In: 2

Permitted impurity max. in wt.%
Al: 0.001 | Bi: 0.030 | Cd: 0.010 | P: 0.008 |
Pb: 0.025 | Si: 0.05

Overall impurity max. in wt.%
0.15

Melting range acc. to ISO 17672 in °C
Not applicable, Why?

Melting range acc. to DSC measurement in °C
680 – 760

Brazing temperature min. in °C
710

Shear strength² acc. to DIN EN 12797 in MPa
> 150

Density in g/cm³
8.7

 

1) The data on the silver content of sandwich brazing alloys refer only to the brazing layer.

2) Measured according to BrazeTec standard, compound 1.2210 & K10;

Less Silver
–21 wt. %










Same
Strength

More Brazing Alloy
+3.1 %
 
Less
Costs

Quotation

.
Standard BrazeTec 49/Cu

Composition¹ in wt.%
Ag: 49 | Cu: 27.5 | Zn: 20.5 | Mn: 2.5 | NI: 0.5 | In: –

Permitted impurity max. in wt.%
Al: 0.001 | Bi: 0.030 | Cd: 0.010 | P: 0.008 |
Pb: 0.025 | Si: 0.05

Overall impurity max. in wt.%
0.3

Melting range acc. to ISO 17672 in °C

Melting range acc. to DSC measurement in °C
670 – 720

Brazing temperature min. in °C
710

Shear strength² acc. to DIN EN 12797 in MPa
> 150

Density in g/cm³
9.0

 

 


Sandwich alloys, Cd free in comparison: BrazeTec Bluebraze 28/Cu plus zu Standard BrazeTec 49/Cu plus

BrazeTec BlueBraze 28/Cu plus

Composition¹ in wt.%
Ag: 28 | Cu: 39.0 | Zn: 20 | Mn: 10 | Ni: 1 | In: 2

Permitted impurity max. in wt.%
Al: 0.001 | Bi: 0.030 | Cd: 0.010 | P: 0.008 |
Pb: 0.025 | Si: 0.05

Overall impurity max. in wt.%
0.15

Melting range acc. to ISO 17672 in °C
Not applicable, Why?

Melting range acc. to DSC measurement in °C
680 – 760

Brazing temperature min. in °C
710

Shear strength² acc. to DIN EN 12797 in MPa
> 180

Density in g/cm³
8.7

 

1) The data on the silver content of sandwich brazing alloys refer only to the brazing layer.

2) Measured according to BrazeTec standard, compound 1.2210 & K10

Less Silver
–21 wt. %










Same
Strength

More Brazing Alloy
+5.5 %
 
Less
Costs

Quaotation

.
Standard BrazeTec 49/Cu plus

Composition¹ in wt.%
Ag: 49 | Cu: 27.5 | Zn: 20.5 | Mn: 2.5 | NI: 0.5 | In: –

Permitted impurity max. in wt.%
Al: 0.001 | Bi: 0.030 | Cd: 0.010 | P: 0.008 |
Pb: 0.025 | Si: 0.05

Overall impurity max. in wt.%
0.3

Melting range acc. to ISO 17672 in °C

Melting range acc. to DSC measurement in °C
670 – 720

Brazing temperature min. in °C
710

Shear strength² acc. to DIN EN 12797 in MPa
> 180

Density in g/cm³
9.0

 

 


Address


Company*

Department

Gender*

Surename*

Name*

Phone*

E-mail*

Street

Nr.

Postal code

City

Comment*mandatory

Informations

Please send me your
BrazeTe BlueBraze brochures



Please contact me by

Phone E-mail

=
Security code.
Please enter the total sum.
 

Address


Company*

Department

Gender*

Surename*

Name*

Phone*

E-mail*

Street*

Nr.*

Postal code*

City*

Comment*mandatory

Traid Fair

Please send me tickets for the trade fair


Ligna, Hannover


I will visit you at the trade fair on:

Date, Approx. Time

Preferred Contact (if known)

=
Security code. Please enter the total sum.

 

Thank you!

We have received your message.

 

aim